JIS G3445 Karbonli po'latdan choksiz mexanik quvurlar
Nima uchun JIS G3445 karbonli po'latdan yasalgan choksiz po'lat quvur mashinasozlik sohasida afzalliklarga ega?
1. JIS G3445 standarti bo'yicha po'lat quvur materiallari asosan past{2}}karbonli po'latdir, masalan, STKM11A/STKM13 seriyali, payvandlash uglerod ekvivalenti (CE)<0.35%, which can be welded without preheating, which can significantly reduce the processing cost. Compared with the same grade of carbon steel pipe, the cost is about 25% lower than ASTM A106 (because the high-temperature performance testing cost is saved).
2. STKM12C gidravlik silindrlar uchun eng yaxshi material tanlovidir. JIS G3445 karbonli po'latdan yasalgan choksiz po'lat quvurning bardoshliligi sovuq chizish jarayoni orqali ± 0,15 mm da nazorat qilinadi, ASTM A53 esa bir xil ishlov berish texnologiyasi ostida qo'shimcha silliqlashni talab qiladi. JIS G3445 32MPa dan kam yoki unga teng boʻlgan gidravlik silindr korpuslari uchun -aniq sovuq chizish jarayoni bilan tejamkor tanlovga aylandi.
3. JIS G3445 karbonli po'latdan yasalgan choksiz quvur shtamplash va bükme kabi chuqur ishlov berishni qo'llab-quvvatlaydi va avtomobillarning shassi qavslari va korpus ramkalarini shakllantirish uchun ishlatilishi mumkin.
Ilovalar
JIS G3445 uglerod po'latdan choksiz mexanik trubkasi sanoatning keng doirasi bo'ylab keng ko'lamli ilovalar uchun javob beradi. Bu ilovalarga quyidagilar kiradi:
- Avtomobil qismlari:suspenziya tizimlari, rul ustunlari, qo'zg'aysan vallar va boshqa konstruktiv komponentlar.
- Mashina qismlari:ramkalar, miller va tishli qutilar.
- Qurilish uskunalari:kran bomlari, ko'prik komponentlari va boshqa-og'ir yuklarga mo'ljallangan ilovalar.
- Umumiy muhandislik:konstruktiv ramkalar, konveyer tizimlari va boshqa mexanik ilovalar.
Kimyoviy tarkibi
| Chelik darajasi | Kimyoviy tarkibi | |||
| STKM 11A | C: 0,12% max, Si: 0,35% max, Mn: 0,60% maks, P: 0,040% maks, S: 0,040% maks. | |||
| STKM 12A | C: 0,20% max, Si: 0,35% max, Mn: 0,60% maks, P: 0,040% maks, S: 0,040% maks. | |||
| STKM 12B | C: 0,20% max, Si: 0,35% max, Mn: 0,60% maks, P: 0,040% maks, S: 0,040% maks. | |||
| STKM 12C | C: 0,20% max, Si: 0,35% max, Mn: 0,60% maks, P: 0,040% maks, S: 0,040% maks. | |||
| STKM 13A | C: 0,25% max, Si: 0,35% max, Mn: 0,30-0,90%, P: 0,040% max, S: 0,040% maks. | |||
| STKM 13B | C: 0,25% max, Si: 0,35% max, Mn: 0,30-0,90%, P: 0,040% max, S: 0,040% maks. | |||
| STKM 13C | C: 0,25% max, Si: 0,35% max, Mn: 0,30-0,90%, P: 0,040% max, S: 0,040% maks. | |||
| STKM 15A | C: 0,25% max, Si: 0,35% max, Mn: 1,30% maks, P: 0,040% maks, S: 0,040% maks. | |||
Mexanik xususiyatlar
| Chelik darajasi | Kuchlanish kuchi (MPa) | Hosildorlik (MPa) | Uzayish (%) |
| STKM 11A | 290 min | 180 min | 25 min |
| STKM 12A | 345 min | 175 min | 35 min |
| STKM 12B | 390 min | 275 min | 25 min |
| STKM 12C | 470 min | 355 min | 20 min |
| STKM 13A | 375 min | 215 min | 30 min |
| STKM 13B | 440 min | 305 min | 20 min |
| STKM 13C | 510 min | 375 min | 20 min |
| STKM 15A | 470 min | 345 min | 20 min |
Mumkin muqobil baholar
JIS G3445 uglerodli po'latdan yasalgan choksiz mexanik quvurlarning keng qamrovini belgilab bergan bo'lsa-da, boshqa xalqaro standartlarda muqobil navlar mavjud. Ko'rib chiqilishi kerak bo'lgan ba'zi potentsial alternativalar ASTM A519, DIN 2391 va BS 6323.
Muayyan ilovalar uchun muqobil navlarni ko'rib chiqishda tegishli standartlarga murojaat qilish va materialning xususiyatlari va texnik xususiyatlarini solishtirish juda muhimdir.
Qadoqlash
Quvurlar barcha tekshiruvlar va sinovlardan o'tgandan so'ng, ular qadoqlash uchun tayyor. Ular odatda plastmassaga o'ralgan balyalarga qadoqlanadi. Quvurlar mijozning talablariga muvofiq yig'ilib, etkazib berishga tayyor bo'lishi mumkin, bu quvurlarni tashish paytida himoyalanganligini va sirt shikastlanishining oldini oladi.